Here is a page of what we found out during sintering, what the manufacuter manufacturer recommends, my thoughts on it, and what to try in a possible future.
Used material: PolyMIM 316L, water debinding feedstock
Used sintering furnace: Mimh Vogt HTS-2/METAL
First of all, here are the debinding and sintering parameters recommended by the manufacturer:
Now, to start with, there are some issues here.
Firstly, the Mim Mimh Vogt sintering oven we got for these experiments can't ramp below 5 K/min, and working with pure hydrogen just isn't feasable in the FabLab.
Therefore we agreed on some compromises, namely ramping with 5 K/min or faster, and using forming gas (95% N2, 5% H2) as a reducing atmosphere.
...
Gas is turned on at 200 °C, and the Cooldown step is necessary to keep gas flowing during cooldown, otherwise the oven would close its valve as soon as the 180 min sintering step is over.
The oven only opens back up once it has reached 200 °C.
Gas flow should be at least 2.0 SLPM, as below that oxidation becomes very evident and parts become brittle.
At ~2.5 SLPM parts come out with partially metallic looking surfaces, maybe testing at even higher flow rates will yield interesting results.
In all experients experiments so far there has not been a visible difference between parts that underwent a debinding process before sintering, and untreated parts.
Debinding has been done at various temperatures and times, with and without corrosion inhibitors, but at least on the small parts we have sintered so far there has been no noticeable difference.
The biggest influence lies in the temperature ramps, both for drying and burning off the binder. If the risetime is too high parts will bend unde uneven heating, as there is no time to reach thermal equilibrium, beyond that they will crack open or burst.
All experiments have been done with the parts just lying on the included sintering beads, maybe burying them under a layer will improve the thermal distribution.
...